Audited Supplier
H600R
R (Surfacing Electrode)
High Chromium Steel
3.2mm
300-400mm
High Chromium Steel
Low Hydrogen Sodium
Acidic
Chromium Stainless Steel
Surfacing Electrode, Low Hydrogen Type Electrode, Hardfacing Electrode
AC/DC
TYUE
5kg/Box, 20kg/Carton
3.2mm x 400mm
Jiangsu, Nantong, China
8311200000
Product Description
Hard-facing H600R
Classification:
DIN 8555 E 6-UM-55
Description:
A rutile coated, hard facing electrode featuring deposits of high toughness and excellent abrasion resistance to medium impact. Positions: flat, horizontal and vertical-up.
Key Facts:
• Provides high toughness in spite of high hardness and excellent abrasion resistance to medium impact.
• Extends the operation life of many wearing parts
• Excellent abrasion resistance to medium impact
• Deposits weld metal of high toughness
• Hard facing electrode 52HRC single layer, 55HRC multiple layers
Applications:
Suitable for surfacing worn parts of civil engineering, construction and mining equipment, without machining. Applications include guillotine blades, punches, dies, pneumatic drills and chisels, axes, ripper teeth, wood chipper anvils and blades and debarking hammers.
Typical All Weld Metal Analysis
Typical All Weld Metal Mechanical Properties:
Single Layer: 52 HRC
Multiple Layer: 55 HRC
Classification:
DIN 8555 E 6-UM-55
Description:
A rutile coated, hard facing electrode featuring deposits of high toughness and excellent abrasion resistance to medium impact. Positions: flat, horizontal and vertical-up.
Key Facts:
• Provides high toughness in spite of high hardness and excellent abrasion resistance to medium impact.
• Extends the operation life of many wearing parts
• Excellent abrasion resistance to medium impact
• Deposits weld metal of high toughness
• Hard facing electrode 52HRC single layer, 55HRC multiple layers
Applications:
Suitable for surfacing worn parts of civil engineering, construction and mining equipment, without machining. Applications include guillotine blades, punches, dies, pneumatic drills and chisels, axes, ripper teeth, wood chipper anvils and blades and debarking hammers.
Typical All Weld Metal Analysis
| C - Carbon | Mn - Manganese | Si - Silicon | Cr - Chromium |
| 0.50% | 1.00% | 0.80% | 7.00% |
Typical All Weld Metal Mechanical Properties:
Single Layer: 52 HRC
Multiple Layer: 55 HRC